Bronze, a copper-tin alloy, widely utilizing in manufacturing of gears, bearing, and packing technologies due to its versatile physical, mechanical, and chemical properties. The aim of the present work was to evaluate the effect of biofield treatment on physical and structural properties of bronze powder. Bronze powder was divided into two samples, one served as control and the other sample was received biofield treatment. Control and treated bronze samples were characterized using x-ray diffraction (XRD), particle size analyzer, scanning electron microscopy (SEM), and Fourier transform infrared (FT-IR) spectroscopy. XRD result showed that the unit cell volume was reduced upto 0.78% on day 78 in treated bronze as compared to control. Further, the crystallite size was significantly reduced upto 49.96% in treated bronze sample on day 106 as compared to control. In addition, the biofield treatment has significantly reduced the average particle size upto 18.22% in treated bronze powder as compared to control. SEM data showed agglomerated and welded particles in control bronze powder, whereas fractured morphology at satellites boundaries were observed in treated bronze. The yield strength of bronze powder calculated using HallPetch equation, was significantly changed after biofield treatment. The FT-IR analysis showed that there were three new peaks at 464 cm-1, 736 cm-1, and 835 cm-1 observed in treated bronze as compared to control; indicated that the biofield treatment may alter the bond properties in bronze. Therefore, the biofield treatment has substantially altered the characteristics of bronze at physical and structural level.
Comments: 6 Pages.
Download: PDF
[v1] 2016-07-13 01:23:34
Unique-IP document downloads: 102 times
Vixra.org is a pre-print repository rather than a journal. Articles hosted may not yet have been verified by peer-review and should be treated as preliminary. In particular, anything that appears to include financial or legal advice or proposed medical treatments should be treated with due caution. Vixra.org will not be responsible for any consequences of actions that result from any form of use of any documents on this website.
Add your own feedback and questions here:
You are equally welcome to be positive or negative about any paper but please be polite. If you are being critical you must mention at least one specific error, otherwise your comment will be deleted as unhelpful.